A Chromium Terephthalate-Based Solid with Unusually Large Pore Volumes and Surface Area

See allHide authors and affiliations

Science  23 Sep 2005:
Vol. 309, Issue 5743, pp. 2040-2042
DOI: 10.1126/science.1116275

This article has a correction. Please see:


We combined targeted chemistry and computational design to create a crystal structure for porous chromium terephthalate, MIL-101, withverylargeporesizes and surface area. Its zeotype cubic structure has a giant cell volume (∼702,000 cubic angstroms), a hierarchy of extra-large pore sizes (∼30 to 34 angstroms), and a Langmuir surface area for N2 of ∼5900 ± 300 square meters per gram. Beside the usual properties of porous compounds, this solid has potential as a nanomold for monodisperse nanomaterials, as illustrated here by the incorporation of Keggin polyanions within the cages.

Porous materials with large, regular, accessible cages and tunnels are increasingly in demand for applications in catalysis (1), separations (2), sensors, electronics, and gas storage (3, 4). Depending on their structure and pore size, these materials allow only molecules of certain shapes and sizes to enter the pores. Furthermore, giant pores may act as nanoreactors, in which the confined volume may generate reactions that do not occur in the bulk material, or as nanomolds for calibrated and monodisperse nanomaterials (5). In this respect, the larger the pores, the wider the range of reactants that can be combined or stored.

However, the design of materials with increasingly large pores carries, especially for metal-organic frameworks, the risk of interpenetration of the skeletons within structures. In addition, although the structural characterization of such solids with large cells is usually possible when single crystals are available, the probability of getting the solutions is known to drastically decrease or even to become zero when the cell dimensions increase too much (6). These problems have restricted the number of discovered porous solids with extra-large pores, of which cloverite, with a cell volume of ∼125,000 Å3 and pore diameters close to 30 Å (7) is the largest.

We recently developed a strategy to overcome these limitations based on the combination of targeted chemistry and computer simulations. Hybrid porous solids result from the three-dimensional (3D) covalent connection of inorganic clusters and organic moieties that act as linkers, and the first step in our “tailor-made” approach is to control the nature of the inorganic cluster and the chemical conditions required for its formation and stability in solution (8). In the second step, we use computational strategies, typically our global optimization AASBU (automated assembly of secondary building units) method (912), as recently adapted to hybrids (13), or other closely related methods (14). The AASBU method explores how an inorganic cluster and an organic linker, or even predefined hybrid building blocks, may connect in 3D space to form periodic lattices. A virtual library of candidate frameworks is produced, along with their crystallographic features (space group, cell parameters, atomic coordinates) and their simulated x-ray diffraction (XRD) patterns. The comparison of the simulated pattern of each candidate structure with the experimental one identifies the targeted experimental structure, giving direct access to the structural solution without any recourse to single crystals. The final structure is refined with the Rietveld method from powder data, the guest species being localized from Fourier difference maps. While tackling the underlying issue of polymorphism of hybrid materials, our computational approach provides a direct-space tool for solving structures that may be highly complex.

To implement our combined method, we first determined (10) the adequate chemical conditions leading to the existence of trimeric inorganic building blocks, formed by the assembly of three octahedra sharing a μ3-O common vertex. Simulations were then performed to combine these inorganic trimers in 3D space with 1,3,5-benzene tricarboxylate (BTC) through the assembly of a computationally designed hybrid building block. Among the various predicted crystal structures, one candidate exhibited the same powder XRD pattern as the powdered chromium trimesate MIL-100 (15) (MIL, Matérial Institut Lavoisier), revealing a giant cell volume (>380,000 Å3) and large pore sizes (∼25 to 29 Å) consistent with the very high surface area measurement (SLangmuir = 3100 m2 g–1). This hybrid crystal structure was then refined from synchrotron powder data, allowing the further localization of the guest moities. MIL-100 showed the feasibility of creating simulation-assisted chemical structures (16). With that adressed, we investigated other carboxylates, here terephthalic acid [1,4-benzene dicarboxylate (1,4-BDC)] combined with similar trimers. Compared to other MOFs (metal-organic frameworks), the resulting solid, MIL-101, has the best characteristics in terms of cell dimensions (702,000 Å3), pore sizes (29 to 34 Å), and surface area (5900 m2 g–1).

The synthesis of MIL-101 consists in the hydrothermal reaction of H2BDC (166 mg at 1 mmol) with Cr(NO3)3.9H2O (400 mg at 1 mmol), fluorhydric acid (0.2 ml at 1 mmol), and H2O (4.8 ml at 265 mmol), for 8 hours at 220°C. This reaction produced a highly crystallized green powder of the chromium terephthalate with formula Cr3F(H2O)2O[(O2C)-C6H4-(CO2)]3.nH2O(where n is ∼25), based on chemical analysis. The yield based on chromium is ∼50%. Analysis of the powder XRD data indicates a cubic cell (a ∼89 Å) and a close relationship with the augmented Mobil Thirty-Nine (MTN) zeotype structure of MIL-100 (17). For the simulation process, a candidate hybrid building block, made on the sole basis of its compatibility with the experimental metal:organic ratio of the targeted MIL-101, was computationally designed as a super tetrahedron (hereafter noted ST) (Fig. 1). It was made from the linkage of 1,4-BDC anions and inorganic trimers that consist of three iron atoms in an octahedral environment with four oxygen atoms of the bidendate dicarboxylates, one μ3O atom, and one oxygen atom from the terminal water or fluorine group. Octahedra are related through the μ3O oxygen atom to form the trimeric building unit. The four vertices of the ST are occupied by the trimers, and the organic linkers are located at the six edges of the ST. Following our previous strategy (14), the ST building blocks were computationally assembled. The size of the ST requires an expansion of the cubic unit cell (space group F d-3m) to more than 85 Å before the construction process. The connection between the ST was established through vertices to ensure a 3D network of “corner-sharing” super tetrahedra with an augmented MTN zeotype architecture (18) (Fig. 1) and illustrates our concept of scale chemistry (19). Once the structure construction of MIL-101 was computationally completed (74 atoms per asymmetric unit without hydrogen atoms), the model structure of MIL-101 was directly used for full structural refinement with synchrotron data (table S1 and fig. S1) (20). Free water molecules filling the pores were located through successive Fourier differences.

Fig. 1.

(A) The computationnally designed trimeric building block chelated by three carboxylic functions. The ST was constructed with (B) terephthalic acid, which lies (C) on the edges of the ST. (D) Ball-and-stick representation of one unit cell, highlighting one ST drawn in a polyhedron mode. (E) Schematic 3D representation of the MTN zeotype architecture (the vertices represent the centers of each ST) with the medium (in green, with 20 tetrahedra) and large (in red with 28 tetrahedra) cages delimited by the vertex sharing of the ST. Chromium octahedra, oxygen, fluorine and carbon atoms are in green, red, and blue, respectively.

The STs are microporous (with a ∼8.6 Å free aperture for the windows), and the resulting framework delimits two types of mesoporous cages filled with guest molecules (Fig. 2). These two cages, which are present in a 2:1 ratio, are delimited by 20 and 28 ST (one by 20 and one by 28) with internal free diameters of ∼29 Å and 34 Å, respectively (Fig. 2). These values correspond to accessible pore volumes of ∼12,700 Å3 and ∼20,600 Å3, respectively. The large windows of both cages make the latter accessible to very large molecules. The smaller cages exhibit pentagonal windows with a free opening of ∼12 Å, while the larger cages possess both pentagonal and larger hexagonal windows with a ∼14.5 Å by 16 Å free aperture (Fig. 2).

Fig. 2.

(A and B) Ball-and-stick view and free dimensions (Å) of the pentagonal and hexagonal windows. (C and D) Ball-and-stick view of the two cages. Chromium octahedra, oxygen, fluorine and carbon atoms are in green, red, red and blue, respectively.

Thermogravimetric analysis in air (fig. S2) revealed that MIL-101 was stable up to 275°C. X-ray thermodiffractometry showed that the evacuation of the guest molecules did not affect the framework. We also found that MIL-101 exhibited very high uptake of gases. The N2 sorption isotherm on the dehydrated sample (fig. S3A) is of type I with secondary uptakes at P/P0 ∼0.1 and at P/P0 ∼0.2, where P is gas pressure and P0 is saturation pressure, characteristic of the presence of the two kinds of microporous windows. Using the Dubinin-Raduskhvich equation, we found a pore volume near 2.0(1) cm3 g–1 for MIL-101. The apparent Brunauer Emmer Teller (BET) and SLangmuir surface area are larger than 4,100(200) and 5,900(300) m2 g–1, respectively (Fig. 3). The isotherms are probably overestimating the true internal surface area of MIL-101, but comparisons to be made with related materials are possible. To our knowledge, the highest surface area reported for any crystalline or amorphous solid [4500 m2 g–1 (Langmuir)], was obtained with MOF-177, a porous hybrid solid (20). The large standard deviations for the surface area of MIL-101 comes both from experimental considerations (such as error on weight measurements and purity of the sample) and from the choice of the points used for the BET or Langmuir calculation (fig. S3B). The as-synthesized MIL-101 solid exhibits a smaller SLangmuir surface area within the 4500 to 5500 m2 g–1 range because of the presence of variable amounts of free terephthalic acid outside and within the pores. An activation treatment was thus performed to reach the maximal surface area and pore volume (21).

Fig. 3.

Nitrogen gas sorption isotherm at 78 K for MIL-101. P/PO is the ratio of gas pressure (P) to saturation pressure (P0 = 750 torr).

MIL-101 is stable over months under air atmosphere and was not altered when treated with various organic solvents at room temperature or under solvothermal conditions. These properties, together with high adsorption capacities, make MIL-101 an attractive candidate for the adsorption of gas or large molecules. The very large windows easily allow the introduction of new species into the cages and possible enhanced reactions favored by confinement effects (similar to a pressure) in the cages. Moreover, as soon as introduced nanometric species fill the volume, the fixed dimensions of the pores lead to monodispersed nanomaterials on the scale of 1 to 3 nm. The possibility of their introduction depends on the fit between their size and the accessible dimensions of the windows of each cage. Large species may therefore occupy only the large cages (∼20,600 Å3) while leaving space for other species with different properties in the small cages (∼12,700 Å3). Such a selective placement of guests might lead to hitherto unknown assemblies of monodisperse multifunctional nanomaterials and the possibility of structural characterization of these nano-objects when the host structure is not affected by the introduction of species.

To illustrate this idea, we explored the incorporation of Keggin polyanions in MIL-101. Such incorporation has been achieved previously through the encapsulation of a molybdenum Keggin anion in a metal-oxygen system (22). The K7PW11O40.nH2O salt was selected because of its low acidity, the presence of a 31P nuclear magnetic resonance (NMR) nucleus for NMR characterization, and finally its size (van der Waals radius, ∼13.1 Å), which rules out the diffusion of Keggin ions into the small cages. A powdered sample of MIL-101 was placed in an aqueous solution of the Keggin salt for 2 hours. To probe the presence of the polynanion within the pores, the resulting MIL-101–Keggin solid was analyzed by thermal gravimetric analysis (TGA), N2 sorption measurement, XRD, 31P solid state NMR (Fig. 4), and infrared spectroscopy (fig. S3). All of these techniques confirmed the presence of a large amount of the Keggin ions within the pores: a strong decrease in the weight losses [TGA (fig. S2)] and surface areas [SLangmuir ∼3,750(250) m2 g–1 instead of 5,900(300) m2 g–1 for MIL-101 (fig. S3C)] due to the higher density of the Keggan moieties compared to MIL-101. We observed significant changes in XRD peak intensities but not of the Bragg peak positions (fig. S4). Infrared spectroscopy confirmed the presence of the polyanions within the pores of MIL-101 (fig. S5). 31P NMR also indicated one single peak at about–12.2(1) parts per million (ppm), confirming that the integrity of the Keggin structure was retained within the pores of MIL-101 (fig. S6).

Fig. 4.

(A) Schematic view of the insertion of Keggin anions within the largest pore of MIL-101. (B) XRD of MIL-101 (1) and MIL-101(Keggin) (2). θ, in degrees. (C) TGA of MIL-101 (1) and MIL-101(Keggin) (2). T, temperature (K). (D) Nitrogen sorption-desorption isotherms at 78 K of MIL-101 (1) and MIL-101(Keggin) (2). Vads, volume adsorbed in cm3 g–1. (E) 31P solid-state NMR spectra of the Keggin salt and MIL-101(Keggin). δ, chemical shift in ppm.

Quantitative analysis (17) also gave an estimation of ∼0.05 Keggin anions per chromium. Considering the size of the K7PW11O40 ion, we assumed that the polyanions could diffuse into the largest cages only, which would allow about five highly charged Keggin moities per large cage (Keggin per cage, ∼5.3). Because the volume of a PW11O407– anion is nearly 2250 A3, five Keggin ions represent ∼10,100 A3 in volume, which is lower than the ∼20,600 A3 volume of a large cage. The residual volume is probably occupied by cations and water molecules. This successful incorporation of Keggin anions in large amounts strongly suggests that MIL-101, a crystallized hybrid solid with a periodical and calibrated porosity, is an excellent candidate for the introduction of gas (23) nano-objects in a regular and monodisperse mode with specific physical properties (24) or for drug delivery (25).

Supporting Online Material

Materials and Methods

Figs. S1 to S6

Table S1

References and Notes

References and Notes