Identification of Active Gold Nanoclusters on Iron Oxide Supports for CO Oxidation

See allHide authors and affiliations

Science  05 Sep 2008:
Vol. 321, Issue 5894, pp. 1331-1335
DOI: 10.1126/science.1159639


Gold nanocrystals absorbed on metal oxides have exceptional properties in oxidation catalysis, including the oxidation of carbon monoxide at ambient temperatures, but the identification of the active catalytic gold species among the many present on real catalysts is challenging. We have used aberration-corrected scanning transmission electron microscopy to analyze several iron oxide–supported catalyst samples, ranging from those with little or no activity to others with high activities. High catalytic activity for carbon monoxide oxidation is correlated with the presence of bilayer clusters that are ∼0.5 nanometer in diameter and contain only ∼10 gold atoms. The activity of these bilayer clusters is consistent with that demonstrated previously with the use of model catalyst systems.

Gold nanoparticles on oxide supports are being used to catalyze an increasing number of reactions (16), but there is continuing interest in the relatively simple low-temperature oxidation of CO (13, 7), especially concerning the nature of the active species. Some proposals emphasize the size and morphology of the gold particle and its interface with the support (1, 8), whereas others postulate that the metal oxidation state (9, 10) and support material can have strong effects (1, 11). Most of the fundamental insights into this reaction have come from well-defined model studies (1215) in which specific structures are tailor-made (14). However, the difficulty lies in linking these informative model studies to those carried out on real catalysts, which are inherently more complex. Here, we report a microscopy study of an Au/FeOx catalyst and demonstrate that, among a number of gold nanostructures present, the origin of the activity is associated uniquely with gold bilayer nanoclusters that are ∼ 0.5 nm in diameter and contain ∼10 Au atoms.

Gold supported on FeOOH is a highly active catalyst for the low-temperature oxidation of CO (16), and we recently reported a link between catalyst performance and catalyst drying conditions (10). A pair of 2.9 atomic % Au/FeOx samples (denoted samples 1 and 2) were derived from the same coprecipitated precursor. Sample 1 was dried in a tube furnace (static air; furnace was ramped after insertion at 15°C/min to 120°C; 16 hours), whereas sample 2 was dried in a gas chromatography (GC) oven (flowing air; sample inserted into the furnace at 120°C; 16 hours). The Au loading in each was identical, and the underlying disordered FeOOH supports had similar surface areas (∼190 m2 g–1). X-ray energy-dispersive spectroscopy (XEDS) analysis and high-angle annular dark-field (HAADF) imaging experiments (10) indicated that both samples contained 2- to 15-nm Au particles, with mean particle sizes of 5.4 nm for sample 1 and 7.0 nm for sample 2.

If the CO oxidation activity was dictated solely by the Au particle size, as some researchers have suggested (1, 8), then these two samples should have exhibited similar activities. In fact, sample 1 would probably be expected to have a slightly better performance by virtue of the Au particles being slightly smaller, on average. However, catalytic testing of these two samples under standard conditions (total flow rate of 66,000 h–1; 0.5 volume% CO) revealed that sample 2 achieved 100% CO conversion at 25°C, whereas sample 1 gave only trace CO conversion (<1%). Even at much higher flow rates, sample 2 remained active (i.e., at a total flow rate of 450,000 vol.gas/vol.catalyst.h; the conversion was 25%), whereas sample 1 was totally inactive. Previously (10), we were unable to determine the origin of this marked effect because of the resolution and sensitivity limitations of the characterization techniques available. We consider that at least two possibilities exist to explain this difference: (i) There could be highly dispersed Au species present in sample 2 that were beyond the resolution limit of the conventional HAADF and scanning transmission electron microscopy (STEM)–XEDS techniques used previously, or (ii) the active catalyst contained some form of cationic Au species that was absent in the inactive sample. These two possibilities need not be mutually exclusive.

To investigate this unexpected difference in reactivity, we re-examined the samples using a state-of-the-art JEOL 2200FS in STEM mode equipped with a double-hexapole spherical aberration corrector manufactured by CEOS GmbH (17). The improvement to the HAADF image resolution, from the use of a 0.1-nm diameter aberration-corrected STEM probe containing 50 pA of current, makes this an ideal instrument to test whether there were Au species present in the highly active sample that were not detected earlier (10). Previously, this method has successfully been used to image atomic dispersions in the La/Al2O3, Pt/Al2O3, and Au/TiO2 systems (18). The lower-magnification HAADF images for each of the dried Au/FeOx catalysts (Fig. 1, A and B) confirm the earlier results, with particles between 2 and 15 nm in diameter. However, at higher magnification (Fig. 2, A to D, and figs. S1 and S2), the actual Au particle size distribution and morphology in these samples are quite different. Both samples contain larger (2 to 15 nm) Au particles and a considerable number of individual Au atoms (indicated by white circles) dispersed on the iron oxide surface.

Fig. 1.

Low-magnification aberration-corrected HAADF-STEM images from (A) the inactive, tube furnace catalyst (sample 1) and (B) the highly active, GC oven catalyst (sample 2). Au particle size distribution in both samples appears to be very similar at this magnification.

Fig. 2.

High-magnification aberration-corrected STEM-HAADF images of (A and B) the inactive (sample 1) and (C and D) the active (sample 2) Au/FeOx catalysts acquired with the aberration-corrected JEOL 2200FS. The white circles indicate the presence of individual Au atoms, whereas the black circles indicate subnanometer Au clusters consisting of only a few atoms. Note the presence and image intensity difference of two distinct cluster-types: In (C) there are 0.5 nm higher-contrast clusters, whereas in (D) 0.2- to 0.3-nm low-contrast clusters dominate. This difference indicates that bilayer and monolayer subnanometer Au clusters are present in the active catalyst.

The observation of these individual atoms ensures that we are now resolving all of the types of Au species present. However, in addition a large population of subnanometer Au clusters was found in the active sample 2 (circled in black in Fig. 2, C and D) (see also fig. S1) that was not detected in the inactive sample. These Au clusters, the majority of which were 0.2 to 0.5 nm in diameter, contain at most only a few Au atoms. The contrast level exhibited by the 0.2- to 0.3-nm clusters, which are predominant in Fig. 2D, is similar to that of the individual Au atoms, implying that they are monolayer structures. In comparison, the 0.5-nm clusters highlighted in Fig. 2C exhibit markedly higher contrast in the HAADF image than that of the 0.2- to 0.3-nm clusters, suggesting that these larger clusters are most likely bilayers of Au.

Determination of the exact number of atoms in these various structures is complicated by several factors, including the slight contraction of the Au–Au bond distance known to occur in particles of this size (19). However, a rough estimate is still informative, and bilayers of ∼0.5-nm lateral dimension would contain ∼10 atoms (fig. S3A). In comparison, the 0.2- to 0.3-nm clusters of similar contrast to monolayers could contain about three to four atoms (fig. S3B). In contrast, an estimate based on the volumetric packing density of Au (∼59 atoms/nm3) suggests that the larger nanoparticles (5 to 7 nm) would contain 1900 to 5250 atoms if they have a hemispherical geometry. Thus, the subnanometer clusters and individual atoms observed in the highly active sample represent only a very minor fraction of the total Au content.

We used atomic-resolution STEM imaging to estimate the number fraction of the total Au particles represented by both clusters and nanoparticles by surveying several support areas that had ∼100 larger nanoparticles, along with their neighboring vicinities (17). In terms of their frequency of observation, the individually adsorbed Au atoms represented 44 ± 4.5% of the Au species, whereas 19 ± 3.4% were 0.2- to 0.3-nm clusters, 18 ± 3.0% were 0.3- to 0.5-nm clusters, and 19 ± 3.5% were particles >1 nm (∼50% were >5 nm).

However, considering the number of Au atoms in each of these structures (as discussed above) suggests that the individual atoms represent only 0.13 ± 0.07 atomic % and that the monolayer and bilayer subnanometer clusters combined represent only 1.05 ± 0.72 atomic % of the total Au loading (18), with the remaining 98.82 ± 0.80 atomic % of Au contained in the larger particles. Because of the very large disparity in the number of atoms they contain, the number of subnanometer clusters would have to exceed that of the 5-nm particles by a margin of nearly four to one for them to represent just 2 atomic % of the total Au loading. Therefore, it is probable that these minority Au species would not be easily detected with traditional “bulk” techniques such as extended x-ray absorption fine structure or Mossbauer spectroscopy, or even by surface analysis techniques such as x-ray photoelectron spectroscopy (XPS), because their contribution to the total signal would be minimal compared with that of the larger nanoparticles (17).

The statistical accuracy of the current HAADF analysis must be considered, because undercounting of the subnanometer Au clusters may result from the nature of the STEM imaging process in an aberration-corrected instrument. The ability to detect single atoms on an oxide is highly dependent on the vertical position of the focused electron probe relative to the surface (20). Because adsorbed atoms can be present on either the top or bottom surface of the underlying oxide particle, imaging with single-atom resolution is possible only when one of the surfaces is exactly in focus. Practically, this limitation means that in any given image, single atoms are probably only detected on one surface of the support particle, and atoms on the opposite side may not be visible, whereas larger nanoparticles can be detected on either side of the support over a much wider range of defocus values. In the intermediate case of 0.2- to 0.5-nm clusters, it is not clear if the same narrow defocus range required to resolve individual atoms is necessary. However, even if it is pessimistically assumed that our analysis has detected only 50% of the total number of all the individual Au atoms, the atomically dispersed Au would still represent only 61 ± 3.6% of the total number of Au species, or ∼0.25 ± 0.2 atomic % of the total Au loading.

The observation that the active species in our Au/FeOx catalysts consist of subnanometer clusters differs from numerous earlier investigations that identified 2- to 5-nm particles as the critical “nanostructure.” However, a number of recent experimental and theoretical (2123) studies have suggested that the CO oxidation activity should continue to increase as the Au particle size approaches 1 nm because of the presence of a larger fraction of Au atoms with low coordination in the smaller particles. Low-coordination Au atoms possess a d-band that is closer to the Fermi level than their close-packed counterparts, so they can adsorb O2 molecules more readily. More specifically, Falsig et al. predicted that adsorption energies for CO and O are ideally suited for maximizing the reaction rate of CO oxidation at sixfold coordinated Au corner atoms, whereas the adsorption energies at close-packed Au faces are inferior for this purpose (23). Because clusters smaller than 1 nm should have an even greater fraction of low-coordinated Au atoms, reaching 90% as a cluster size of 0.5 nm is approached, the role of subnanometer clusters may be crucial. Rashkeev et al. (24) have recently presented HAADF evidence that subnanometer mono-, bi-, and trilayer Au clusters coexisted in active Au/TiO2 catalysts, although they were unable to isolate the relative importance of each of these subnanometer species and did not report any spectroscopic measurements to determine the possible role of substrate surface chemistry.

Scanning tunneling microscopy studies on model catalysts by Matthey et al. (15) showed that subtle changes in the chemistry of an oxide surface could alter the energetically favorable Au structures that it stabilized and supported. Specifically, an oxygen-rich TiO2 (110) surface could stabilize a range of Au species from one to seven atoms in size. In contrast, single Au atoms and Au trimers were the only stable configurations on a reduced TiO2 (110) surface, whereas weakly bonded two-dimensional Au raftlike species were the only stable structures on a stoichiometric TiO2 (110) surface. Similar oxygen-rich surfaces to those reported for TiO2 have also been identified for FeOx (25); however, to our knowledge, systematic surface science studies and first-principle calculations of the stable Au structures present on FeOOH or Fe2O3 have not yet been performed.

On the basis of the observations of the two dried catalysts alone, we are unable to definitively comment on whether the bilayer 0.5-nm clusters, the monolayer 0.2- to 0.3-nm clusters, or both are responsible for the high activity observed or whether some subtle substrate chemistry effect is coming into play. Although individual Au atoms and larger (3 to 5 nm) particles are stable on both catalysts, the subnanometer Au clusters were only stable on the surface of catalyst 2 dried under a flowing air. The critical role played by such slight changes in the catalyst preparation route may help to explain the sometimes radically differing activities reported. We have used XPS to probe the nature of the surface species present in both samples. Analysis of the Au(4f) spectra (fig. S4.1) showed that, in both catalysts, the Au(4f7/2) binding energy was 85.1 eV, characteristic of Au+ species. The signal from sample 1 shows some broadening to higher binding energy that probably arose from a small amount of Au3+, most likely present as AuOOH. The presence of hydroxylated Au species in this inactive sample suggests that the lack of air circulation during the drying process inhibits the removal of the hydroxyl species from the catalyst surface, whereas this process occurs more efficiently under flowing air conditions.

This explanation was confirmed by the O(1s) and C(1s) spectra from these samples (figs. S4.2 and S4.3, respectively). Both catalysts exhibit a main O(1s) component characteristic of oxidic oxygen (O2–) at 530.4 eV, together with a shoulder at 531.8 eV. The latter feature originates from a combination of hydroxyl and carbonate species and is much more pronounced in sample 1. The C(1s) spectra, which show clear evidence of carbonate species, are similar for both. Therefore, the higher intensity of the O(1s) shoulder at 531.8 eV in the inactive catalyst 1 arises from the increased presence of hydroxyl groups relative to the active catalyst 2 dried in flowing air. This higher degree of hydroxylation and reduction of sample 1 seems to enhance the ability of the subnanometer clusters to sinter into larger particles and thus deactivate the catalyst. Hence, on the basis of the evidence presented so far, we are unable to determine whether it is the presence of subnanometer clusters or the differing degree of hydroxylation of the support that is controlling the activity.

Three separate portions of the highly active catalyst 2, denoted 3, 4, and 5, were calcined (3 hours at 400°, 550°, and 600°C, respectively). These heat treatments converted the support material to crystalline Fe2O3 and progressively reduced the surface area (catalysts2:190m2 g–1, 3:45m2 g–1, 4: 16 m2 g–1, and 5: 11 m2 g–1). Atomic absorption spectroscopy confirmed that all of the Au (2.9 atomic %) was retained. CO conversion decreased from 100% in the fresh, uncalcined state to 91% (400°C), 31% (550°C), and <1% (600°C). Aberration-corrected STEM-HAADF images (Fig. 3, A to F, and figs. S5.1 to 5.3) revealed that, although substantial particle sintering had occurred in all calcined catalysts, each sample also retained a population of the subnanometer clusters and individual Au atoms previously seen in the dried catalyst that had persisted through the various calcination treatments.

Fig. 3.

Aberration-corrected STEM-HAADF images of the active 2.9 atomic % Au/FeOx catalyst 2 calcined for 3 hours at (A and B) 400°C (sample 3), (C and D) 550°C (sample 4), and (E and F) 600°C (sample 5). The heat-treatment procedures have substantially decreased the population of subnanometer Au clusters relative to the highly active, dried catalyst, while at the same time they have increased the population of particles in the 1- to 3-nm range.

The number frequency of the various gold species encountered in samples 2, 3, 4, and 5 is summarized in Fig. 4. The number fraction of atomically dispersed species drops from ∼44% to 35% across this sample set, whereas, simultaneously, the number fraction of particles greater than 1 nm progressively increases from 19 to 35%. However, our previous deductions from comparing samples 1 and 2 indicate that the supported subnanometer cluster species (and not the dispersed Au atoms or >1-nm particles) are active for CO conversion. It is also apparent from Fig. 4 that the number population of monolayer clusters remains relatively constant at ∼19%, whereas the bilayer cluster frequency gradually drops from 18% to <5% across this same sample set. Hence, the dramatic decrease in catalytic activity exhibited by samples 3, 4 and 5 can be directly correlated to the marked decrease in the number density of the 0.5-nm bilayer clusters as a result of their sintering into less active 1- to 2-nm Au particles.

Fig. 4.

Relative populations of (i) dispersed Au atoms, (ii) 0.2- to 0.3-nm monolayer Au clusters, (iii) 0.5-nm bilayer Au clusters, and (iv) Au nanoparticles >1 nm in diameter, as a function of catalyst calcination temperature and measured CO conversion. The error bars correspond to two SDs on the size measurements.

XPS of samples 3, 4, and 5 (fig. S6) showed no notable difference in either of the Au(4f), Fe(3s), or Fe(2p) profiles (fig. S6.1 and 6.2) associated with this series of calcined catalysts. The O(1s) signals (fig. S6.3) are also all similar, with a high–binding energy tail indicating the presence of some residual hydroxyl and carbonate species, but these are very different from the dried sample (spectra shown in Fig. 5). The presence of carbonate species is confirmed by the weak, high binding feature in the C(1s) spectra (fig. S6.4). This feature is broader for sample 5, possibly reflecting carbonate species in distinct chemical environments, and is consistent with small differences in the high–binding energy tail in the O(1s) spectrum for this sample.

Fig. 5.

O(1s) photoemission spectra from the Au/Fe2O3 catalysts (A) dried at 120°C and then calcined at (B) 400°C, (C) 550°C, and (D) 600°C.

To determine whether the small differences in samples 3 and 4 and the larger differences with the other samples correlate with the catalytic performance, we deconvoluted the O 1s signals into oxide and the higher–binding energy hydroxyl and carbonate species to obtain the relative fractions of each species present. However, the data for either the relative area percent of the higher–binding energy species (samples 2: 60%, 3: 28%, 4: 34%, and 5: 47%) or the hydroxyl/oxide ratio (samples 2: 1.5, 3: 0.4, 4: 0.5, and 5: 0.9) do not correlate with the observed activity trend. Thus, the similarity in the surface chemistry of samples 3 and 4, in particular, and the Au oxidation state in these calcined samples strongly imply that the progressive decrease in catalytic activity upon sintering is attributable to the gradual decrease in the population of the subnanometer bilayer clusters of gold.

Theoretical and model studies (23, 2629) have shown that a critical factor in the catalytic activity of Au is the ability of the clusters to simultaneously adsorb both reactant molecules. Yoon et al. and Hakkinen et al. (27, 28) showed that the smallest Au cluster on MgO known to be active for CO oxidation is an octamer. Our observations are consistent with these theoretical studies, because the active bilayer subnanometer clusters in our system contain ∼10 atoms, whereas the monolayer clusters (which have only three to four atoms) and the isolated Au atoms appear to be essentially inactive for CO oxidation.

Finally, CO oxidation activity of model Au catalysts on TiO2 surfaces is maximized when the Au structures are two atomic layers thick (14, 28, 29), resulting in turnover frequencies (TOFs) as high as 3.7 s–1. In the present case, the TOF of catalyst 2 exhibiting 100% CO conversion was initially calculated to be 0.016 s–1 under standard conditions and 0.027 s–1 at the higher flow rate where total conversion (which is a more reliable estimate of the catalyst activity) was not observed. However, if the TOF is recalculated assuming that the bilayer clusters are the only active species and using a reasonable estimate of the fraction of the total Au that they contain (0.6 atomic %), the result is a TOF of 2.7 s–1 at the standard conditions and 3.5 s–1 at the higher–flow rate condition. These re-estimated TOF values are reasonably similar to the value of 3.7 s–1 of the model Au/TiO2 catalyst (14).

These studies describe the full range of active and inactive Au species that are present within supported Au/FeOx and Au/Fe2O3 catalysts. Subtle changes in sample-preparation route and calcination temperature can influence the formation, stability, and relative population of these various Au species. Herein, we have reported that highly active subnanometer Au clusters can be synthesized with a traditional chemical preparation route. Although the highest-activity catalysts correspond to uncalcined materials, experiments involving systematic calcination treatments have allowed us to deduce that it is primarily the 0.5-nm bilayer clusters, rather than 0.2- to 0.3-nm monolayer Au clusters, that are active for CO oxidation on FeOx supports.

Supporting Online Material

Materials and Methods

Figs. S1 to S6